The catalytic synthesis of 1,3-diaminopropane from 1,3-propanediol and ammonia was studied in a continuous fixed-bed reactor in the pressure range 50 to 150 bar. The unsupported Co-based catalysts applied were characterized by N₂physisorption, XRD, XPS, TPR, and ammonia adsorption using pulse thermal analysis and DRIFT spectroscopy. The latter investigations revealed that the best catalyst, 95 wt% Co–5 wt% Fe, contained only very weak acidic sites, unable to chemisorb ammonia. The absence of strong acidic and basic sites was crucial to suppress the various acid/base-catalyzed side reactions (retro-aldol reaction, hydrogenolysis, alkylation, disproportionation, dimerization, oligomerization). Other important requirements for improved diaminopropane formation were the use of excess ammonia (molar ratio NH₃/diol>20) and the presence of the metastable β-Co phase. A small amount of Fe additive could efficiently hinder the transformation of this phase into the thermodynamically stable α-Co phase and thus prevent catalyst deactivation up to 10 days on stream. Application of supercritical ammonia almost doubled the selectivity to amino alcohol and diamine. The selectivity enhancement in the near-critical region is attributed to elimination of the interphase mass transport limitations and to the resulting higher surface ammonia concentration.

Polymeric two- and three-dimensional, homo- and heterometallic oxalatebridged coordination compounds offer exciting opportunities, mainly in the fields of molecular magnetism and photophysics. Given that a large variety of magnetic phenomena have been reported so far from these molecular magnets, very limited experience is gained from elastic neutron scattering experiments. Therefore, with two examples, we will address the topic of the elucidation of magnetic structures by means of the neutron scattering technique. In addition, due to the possibility of the variation of different metal ions in varying oxidation states, interesting photophysical processes can be observed within the extended three-dimensional host/guest systems.